Hydrocarbon conversion with an acidic multimetallic catalytic composite

ABSTRACT

Hydrocarbons are converted by contacting them at hydrocarbon conversion conditions with an acidic multimetallic catalytic composite comprising a combination of catalytically effective amounts of a platinum or palladium component, a rhodium component, a rhenium component, a tin component, and a halogen component with a porous carrier material. The platinum or palladium component, rhodium component, rhenium component, tin component, and halogen component are present in the multimetallic catalyst in amounts respectively, calculated on an elemental basis, corresponding to about 0.01 to about 2 wt. % platinum or palladium metal, about 0.01 to about 2 wt. % rhodium, about 0.01 to about 2 wt. % rhenium, about 0.01 to about 5 wt. % tin, and about 0.1 to about 3.5 wt. % halogen. Moreover, these metallic components are uniformly dispersed throughout the porous carrier material in carefully controlled oxidation states such that substantially all of the platinum or palladium component is present therein in the elemental metallic state, substantially all of the rhenium and rhodium components are present therein in the elemental metallic state or in a state which is reducible to the elemental metallic state under hydrocarbon conversion conditions or in a mixture of these states and substantially all of the tin component is present in an oxidation state above that of the elemental metal and in a particle size which is less than 100 Angstroms in maximum dimension. A specific example of the type of hydrocarbon conversion process disclosed is a process for the catalytic reforming of a low-octane gasoline fraction wherein the gasoline fraction and a hydrogen stream are contacted with the acidic multimetallic catalyst disclosed herein at reforming conditions.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application is a continuation-in-part of my prior copending application Ser. No. 480,793 filed June 19, 1974, now U.S. Pat. No. 3,898,154, which in turn is a continuation-in-part of my prior application Ser. No. 376,841 filed July 5, 1973, and now U.S. Pat. No. 3,846,283, which in turn is a continuation-in-part of my prior application Ser. No. 201,576 filed Nov. 23, 1971, and now U.S. Pat. No. 3,745,112, and which in turn is a continuation-in-part of my prior application Ser. No. 807,910 filed Mar. 17, 1969, and now U.S. Pat. No. 3,740,328. All of the teachings of these prior applications are specifically incorporated herein by reference.

DISCLOSURE

The subject of the present invention is a novel acidic multi-metallic catalytic composite which has exceptional activity and resistance to deactivation when employed in a hydrocarbon conversion process that requires a catalyst having both a hydrogenation-dehydrogenation function and a cracking function. More precisely, the present invention involves a novel dual-function acidic multimetallic catalytic composite which, quite surprisingly, enables substantial improvements in hydrocarbon conversion processes that have traditionally used a dual-function catalyst. In another aspect, the present invention comprehends the improved processes that are produced by the use of an acidic catalytic composite comprising a combination of catalytically effective amounts of a platinum or palladium component, a rhodium component, a rhenium component, a tin component, and a halogen component with a porous carrier material; specifically, an improved reforming process which utilizes the subject catalyst to improve activity, selectivity, and stability characteristics.

Composites having a hydrogenation-dehydrogenation function and a cracking function are widely used today as catalysts in many industries, such as the petroleum and petrochemical industry, to accelerate a wide spectrum of hydrocarbon conversion reactions. Generally, the cracking function is throught to be associated with an acid-acting material of the porous, adsorptive, refractory oxide type which is typically utilized as the support or carrier for a heavy metal component such as the metals or compounds of metals of Groups V through VIII of the Periodic Table to which are generally attributed the hydrogenation-dehydrogenation function.

These catalytic composites are used to accelerate a wide variety of hydrocarbon conversion reactions such as hydrocracking, isomerization, dehydrogenation, hydrogenation, desulfurization, cyclization, polymerization, alkylation, cracking, hydroisomerization, etc. In many cases, the commercial applications of these catalysts are in processes where more than one of the reactions are proceeding simultaneously. An example of this type of process is reforming wherein a hydrocarbon feed stream containing paraffins and naphthenes is subjected to conditions which promote dehydrogenation of naphthenes to aromatics, dehydrocyclization of paraffins to aromatics, isomerization of paraffins and naphthenes, hydrocracking of naphthenes and paraffins, and the like reactions, to produce an octane-rich or aromatic-rich product stream. Another example is a hydrocracking process wherein catalysts of this type are utilized to effect selective hydrogenation and cracking of high molecular weight unsaturated materials, selective hydrocracking of high molecular weight materials, and other like reactions, to produce a generally lower boiling, more valuable output stream. Yet another example is an isomerization process wherein a hydrocarbon fraction which is relatively rich in straight-chain paraffins is contacted with a dual-function catalyst to produce an output stream rich in isoparaffin compounds.

Regardless of the reaction involved or the particular process involved, it is of critical importance that the dual-function catalyst exhibit not only the capability to initially perform its specified functions, but also that it has the capability to perform them satisfactorily for prolonged periods of time. The analytical terms used in the art to measure how well a particular catalyst performs its intended functions in a particular hydrocarbon reaction environment are activity, selectivity, and stability. And for purposes of discussion here, these terms are conveniently defined for a given charge stock as follows: (1) activity is a measure of the catalyst's ability to convert hydrocarbon reactants into products at a specified severity level where severity level means the conditions used--that is, the temperature, pressure, contact time, and presence of diluents such as H₂ ; (2) selectivity refers to the amount of desired product or products obtained relative to the amount of reactants charged or converted; (3) stability refers to the rate of change with time of the activity and selectivity parameters--obviously, the smaller rate implying the more stable catalyst. In a reforming process, for example, activity commonly refers to the amount of conversion that takes place for a given charge stock at a specified severity level and is typically measured by octane number of the C₅ + product stream; selectivity refers to the amount of C₅ + yield, relative to the amount of the charge, that is obtained at the particular activity or severity level; and stability is typically equated to the rate of change with time of activity, as measured by octane number of C₅ + product, and of selectivity as measured by C₅ + yield. Actually, the last statement is not strictly correct because generally a continuous reforming process is run to produce a constant octane C₅ + product with severity level being continuously adjusted to attain this result; and furthermore, the severity level is for this process usually varied by adjusting the conversion temperature in the reaction zone so that, in point of fact, the rate of change of activity finds response in the rate of change of conversion temperatures and changes in this last parameter are customarily taken as indicative of activity stability.

As is well known to those skilled in the art, the principal cause of observed deactivation or instability of a dual-function catalyst when it is used in a hydrocarbon conversion reaction is associated with the fact that coke forms on the surface of the catalyst during the course of the reaction. More specifically, in these hydrocarbon conversion processes, the conditions utilized typically result in the formation of heavy, high molecular weight, black, solid or semi-solid, carbonaceous material which is a hydrogen-deficient polymeric substance having properties akin to both polynuclear aromatics and graphite. This material coats the surface of the catalyst and thus reduces its activity by shielding its active sites from the reactants. In other words, the performance of this dual-function catalyst is sensitive to the presence of carbonaceous deposits or coke on the surface of the catalyst. Accordingly, the major problem facing workers in this area of the art is the development of more active and selective catalytic composites that are not as sensitive to the presence of these carbonaceous materials and/or have the capability to suppress the rate of the formation of these carbonaceous materials on the catalyst. Viewed in terms of performance parameters, the problem is to develop a dual-function catalyst having superior activity, selectivity, and stability. In particular, for a reforming process the problem is typically expressed in terms of shifting and stabilizing the C₅ + yield-octane relationship at the lowest possible severity level--C₅ + yield being representative of selectivity and octane being proportional to activity.

I have now found a dual-function acidic multimetallic catalyst composite which possesses improved activity, selectivity, and stability characteristics when it is employed in a process for the conversion of hydrocarbons of the type which have heretofore utilized dual-function acidic catalytic composites such as processes for isomerization, hydroisomerization, dehydrogenation, desulfurization, denitrogenization, hydrogenation, alkylation, dealkylation, disproportionation, polymerization, hydrodealkylation, transalkylation, cyclization, dehydrocyclization, cracking, hydrocracking, halogenation, reforming, and the like processes. In particular, I have ascertained that an acidic catalyst, comprising a combination of catalytically effective amounts of a platinum or palladium component, a rhodium component, a rhenium component, a tin component, and a halogen component with a porous refractory carrier material, can enable the performance of hydrocarbon conversion processes utilizing dual-function catalysts to be substantially improved if the metallic components are uniformly dispersed throughout the carrier material and if their oxidation states are controlled to be in the states hereinafter specified. Moreover, I have determined that an acidic catalytic composite, comprising a combination of catalytically effective amounts of a platinum or palladium component, a rhenium component, a rhodium component, a tin component, and a chloride component with an alumina carrier material, can be utilized to substantially improve the performance of a reforming process which operates on a low-octane gasoline fraction to produce a high-octane aromatic-rich reformate if the metallic components are uniformly dispersed throughout the alumina carrier material, and if the oxidation states of the metallic components are fixed in the states hereinafter specified. In the case of a reforming process, the principal advantage associated with the use of the present invention involves the acquisition of the capability to operate in a stable manner in a high severity operation; for example, a low pressure reforming process designed to produce a C₅ + reformate having an octane of about 100 F-1 clear. As indicated, the present invention essentially involves the finding that the addition of a combination of a rhenium component, a tin component, and a rhodium component to a dual-function acidic hydrocarbon conversion catalyst containing a platinum or palladium component can enable the performance characteristics of the catalyst to be sharply and materially improved, if the hereinafter specified limitations on amounts of ingredient, oxidation states of metals, and disribution of metallic components in the support are met.

It is, accordingly, one object of the present invention to provide an acidic multimetallic hydrocarbon conversion catalyst having superior performance characteristics when utilized in a hydrocarbon conversion process. A second object is to provide a catalyst having dual-function hydrocarbon conversion performance characteristics that are relatively insensitive to the deposition of hydrocarbonaceous material thereon. A third object is to provide preferred methods of preparation of this catalytic composite which insures the achievement and maintenance of its properties. Another object is to provide an improved reforming catalyst having superior activity, selectivity, and stability attributes. Yet another object is to provide a dual-function hydrocarbon conversion catalyst which utilizes a combination of a rhenium component, a tin component, and a rhodium component under specified circumstances to promote an acidic catalyst containing a platinum or palladium component.

In brief summary, the present invention is, in one embodiment, an acidic catalytic composite comprising a porous carrier material containing, on an elemental basis, about 0.01 to about 2 wt. % platinum or palladium metal, about 0.01 to about 2 wt. % rhodium metal, about 0.01 to about 2 wt. % rhenium, about 0.01 to about 5 wt. % tin, and about 0.1 to about 3.5 wt. % halogen, wherein the platinum or palladium, rhenium, tin, and rhodium are uniformly dispersed throughout the porous carrier material, wherein substantially all of the platinum or palladium is present in the elemental metallic state, wherein substantially all of the rhenium and rhodium are present in the elemental metallic state or in a state which is reducible to the elemental metallic state under hydrocarbon conversion conditions or in a mixture of these states, and wherein substantially all of the tin is present in an oxidation state above that of the elemental metal and in a particle size which is less than 100 Angstroms in maximum dimension.

A second embodiment relates to an acidic catalytic composite comprising a porous carrier material containing, on an elemental basis, about 0.05 to about 1 wt. % platinum metal, about 0.01 to about 1 wt. % rhodium metal, about 0.05 to about 1 wt. % rhenium, about 0.05 to about 1 wt. % tin, and about 0.5 to about 1.5 wt. % halogen, wherein the platinum, rhenium, tin, and rhodium are uniformly dispersed throughout the porous carrier material, wherein substantially all of the platinum is present in the elemental metallic state, wherein substantially all of the rhenium and rhodium are present in the elemental metallic state or in a state which is reducible to the elemental metallic state under hydrocarbon conversion conditions or in a mixture of these states and wherein substantially all of the tin is present in an oxidation state above that of the elemental metal and in a particle size which is less than 100 Angstroms in maximum dimension.

Another embodiment relates to an acidic catalytic composite comprising a combination of the catalytic composite described in the first or second embodiment with a sulfur component in an amount sufficient to incorporate about 0.01 to about 1 wt. % sulfur, calculated on an elemental basis.

Yet another embodiment relates to a process for the conversion of a hydrocarbon comprising contacting the hydrocarbon and hydrogen with the catalytic composite described above in the first or second or third embodiment at hydrocarbon conversion conditions.

A preferred embodiment relates to a process for reforming a gasoline fraction which comprises contacting the gasoline fraction and hydrogen with the catalytic composite described above in the first or second or third embodiment at reforming conditions selected to produce a high-octane reformate.

Other objects and embodiments of the present invention relate to additional details regarding preferred catalytic ingredients, preferred amounts of ingredients, suitable methods of composite preparation, operating conditions for use in the hydrocarbon conversion processes, and the like particulars, which are hereinafter given in the following detailed discussion of each of these facets of the present invention.

The acidic multimetallic catalyst of the present invention comprises a porous carrier material or support having combined therewith catalytically effective amounts of a platinum or palladium component, a rhodium component, a rhenium component, a tin component, and a halogen component.

Considering first the porous carrier material utilized in the present invention, it is preferred that the material be a porous, adsorptive, high-surface area support having a surface area of about 25 to about 500 m² /g. The porous carrier material should be relatively refractory to the conditions utilized in the hydrocarbon conversion process, and it is intended to include within the scope of the present invention carrier materials which have traditionally been utilized in dual-function hydrocarbon conversion catalysts such as: (1) activated carbon, coke, or charcoal; (2) silica or silica gel, silicon carbide, clays, and silicates including those synthetically prepared and naturally occurring, which may or may not be acid treated, for example, attapulgus clay, china clay, diatomaceous earth, fuller's earth, kaolin, kieselguhr, etc., (3) ceramics, porcelain, crushed firebrick, bauxite; (4) refractory inorganic oxides such as alumina, titanium dioxide, zirconium dioxide, chromium oxide, beryllium oxide, vanadium oxide, cesium oxide, hafnium oxide, zinc oxide, magnesia, boria, thoria, silica-alumina, silica-magnesia, chromia-alumina, alumina-boria, silica-zirconia, etc.; (5) crystalline zeolitic aluminosilicates such as naturally occurring or synthetically prepared mordenite and/or faujasite, either in the hydrogen form or in a form which has been treated with multivalent cations; (6) spinels such as MgAl₂ O₄, FeAl₂ O₄, ZnAl₂ O₄, MnAl₂ O₄, CaAl₂ O₄, and other like compounds having the formula MO.sup.. Al₂ O₃ where M is a metal having a valence of 2; and, (7) combinations of elements from one or more of these groups. The preferred porous carrier materials for use in the present invention are refractory inorganic oxides, with best results obtained with an alumina carrier material. Suitable alumina materials are the crystalline aluminas known as gamma-, eta-, and theta-alumina, with gamma- or eta-alumina giving best results. In addition, in some embodiments the alumina carrier material may contain minor proportions of other well known refractory inorganic oxides such as silica, zirconia, magnesia, etc.; however, the preferred support is substantially pure gamma- or eta-alumina. Preferred carrier materials have an apparent bulk density of about 0.3 to about 0.7 g/cc and surface area characteristics such that the average pore diameter is about 20 to 300 Angstroms, the pore volume is about 0.1 to about 1 cc/g, and the surface area is about 100 to about 500 m² /g. In general, best results are typically obtained with a gamma-alumina carrier material which is used in the form of spherical particles having: a relatively small diameter (i.e. typically about 1/16 inch), an apparent bulk density of about 0.3 to about 0.8 g/cc, a pore volume of about 0.4 ml/g, and a surface area of about 200 m² /g.

The preferred alumina carrier material may be prepared in any suitable manner and may be synthetically prepared or natural occurring. Whatever type of alumina is employed, it may be activated prior to use by one or more treatments including drying, calcination, steaming, etc., and it may be in a form known as activated alumina, activated alumina of commerce, porous alumina, alumina gel, etc. For example the alumina carrier may be prepared by adding a suitable alkaline reagent, such as ammonium hydroxide, to a salt of aluminum such as aluminum chloride, aluminum nitrate, etc., in an amount to form an aluminum hydroxide gel which upon drying and calcining is converted to alumina. The alumina carrier may be formed in any desired shape such as spheres, pills, cakes, extrudates, powders, granules, tablets, etc., and utilized in any desired size. For the purpose of the present invention a particularly preferred form of alumina is the sphere; and alumina spheres may be continuously manufactured by the well known oil drop method which comprises: forming an alumina hydrosol by any of the techniques taught in the art and preferably by reacting aluminum metal with hydrochloric acid, combining the resultant hydrosol with a suitable gelling agent and dropping the resultant mixture into an oil bath maintained at elevated temperatures. The droplets of the mixture remain in the oil bath until they set and form hydrogel spheres. The spheres are then continuously withdrawn from the oil bath and typically subjected to specific aging treatments in oil and an ammoniacal solution to further improve their physical characteristics. The resulting aged and gelled particles are then washed and dried at a relatively low temperature of about 300° F, to about 400° F. and subjected to a calcination procedure at a temperature of about 850° F. to about 1300° F. for a period of about 1 to about 20 hours. This treatment effects conversion of the alumina hydrogel to the corresponding crystalline gamma-alumina. See the teachings of U.S. Pat. No. 2,620,314 for additional details.

One essential ingredient of the present catalytic composite is a rhenium component. It is of fundamental importance that substantially all of the rhenium component exists within the catalytic composite of the present invention in the elemental metallic state or in a state which is reducible to the elemental state under hydrocarbon conversion conditions or in a mixture of these states. The rhenium component may be utilized in the composite in any amount which is catalytically effective, with the preferred amount being about 0.01 to about 2 wt. % thereof, calculated on an elemental basis. Typically, best results are obtained with about 0.05 to about 1 wt. % rhenium. It is additionally preferred to select the specified amount of rhenium from within this broad weight range as a function of the amount of the platinum or palladium component, on an atomic basis, as is explained hereinafter.

This rhenium component may be incorporated into the catalytic composite in any suitable manner known to those skilled in the catalyst formulation art which results in a relatively uniform distribution of rhenium in the carrier material such as by coprecipitation, ion-exchange, or impregnation. In addition, it may be added at any stage of the preparation of the composite--either during preparation of the carrier material or thereafter--and the precise method of incorporation used is not deemed to be critical. However, best results are obtained when the rhenium component is relatively uniformly distributed throughout the carrier material in a relatively small particle size, and the preferred procedures are the ones known to result in a composite having this relatively uniform distribution. One acceptable procedure for incorporating this component into the composite involves cogelling or coprecipitating the rhenium component during the preparation of the preferred carrier material, alumina. This procedure usually comprehends the addition of a soluble, decomposable compound of rhenium such as perrhenic acid or a salt thereof to the alumina hydrosol before it is gelled. The resulting mixture is then finished by conventional gelling, aging, drying, and calcination steps as explained hereinbefore. A preferred way of incorporating this component is an impregnation step wherein the porous carrier material is impregnated with a suitable rhenium-containing solution either before, during, or after the carrier material is calcined. Preferred impregnation solutions are aqueous solutions of water soluble, decomposable rhenium compounds such as ammonium perrhenate, sodium perrhenate, potassium perrhenate, potassium rhenium oxychloride (K₂ ReOCl₅), potassium hexachlororhenate (IV), rhenium chloride, rhenium heptoxide, and the like compounds. Best results are ordinarily obtained when the impregnation solution is an aqueous solution of perrhenic acid. This component can be added to the carrier material either prior to, simultaneously with, or after the other metallic components are combined therewith. Best results are usually achieved when this component is added simultaneously with the platinum or palladium metallic and rhodium components. In fact, excellent results are obtained with a one step impregnation procedure using a tin-containing alumina carrier material and an acidic aqueous solution containing chloroplatinic acid, perrhenic acid, rhodium trichloride hydrate, and hydrochloric acid.

A second essential constituent of the acidic multimetallic catalytic composite used in the present invention is a tin component, and it is an essential feature of the present invention that substantially all of the tin component in the composite is in an oxidation state above that of the elemental metal. That is, it is believed that best results are obtained when substantially all of the tin component exists in the catalytic composite in the +2 or +4 oxidation state. Accordingly, the tin component will be present in the composite as a chemical compound such as the oxide, hydroxide, sulfide, halide, oxyhalide, oxysulfide, and the like, wherein the tin moiety is in a positive oxidation state, or in chemical combination with the carrier material in a manner such that the tin component is in a positive oxidation state. Controlled reduction experiments with the catalytic composites produced by the preferred methods of preparing the instant catalytic composite have established that the tin component in these catalysts is in a positive oxidation state and is not reduced by contact with hydrogen at temperatures in the range of 1000° to 1200° F. It is important to note that this limitation on the oxidation state of the tin component requires extreme care in preparation and use of the present catalyst to insure that it is not subjected to a reducing atmosphere at temperatures above 1200° F. Equally significant is my observation that it is only when the tin component is in a uniformly dispersed state in the carrier material that it has the capability to maintain its positive oxidation state when subjected to hereinafter described prereduction step. Stated another way, if the tin component is not properly dispersed on the support it can be reduced in the prereduction step and result in an inferior catalyst. Based on the evidence currently available it is believed that best results are obtained when the tin component is present in the catalyst as tin oxide. The term "tin oxide" as used herein refers to a coordinated tin-oxygen complex which is not necessarily stoichiometric.

Interrelated with this oxidation state limitation are the factors of dispersion of the tin component in the support and of particle size of the tin component. This interrelationship emanates from my observation that it is only when the tin component is uniformly dispersed throughout the carrier material in a particle size having a maximum dimension less than 100 Angstroms that it can successfully maintain its preferred oxidation state when it is subjected to a high temperature prereduction treatment as hereinafter described. Thus it is an essential feature of my invention that the instant multimetallic catalytic composite is prepared in a manner selected to meet the stated particle size and uniform dispersion limitations. By the use of the expression "uniform dispersion of the tin component in the carrier material" it is intended to described the situation where the concentration of the tin ingredient is approximately the same in any reasonably divisiable portion of the carrier material. Similarly, the expression "particles having a maximum dimension less than 100 Angstroms" is intended to denote particles that would pass through a sieve having a 100 Angstrom mesh size if it were possible to make such a sieve.

The tin component may be incorporated into the catalytic composite in any suitable manner known to effectively disperse this component throughout the carrier material in the required particle size. Thus this component may be added to the carrier by coprecipitation or cogellation of a suitable soluble tin salt with the carrier material, by ion-exchange of suitable tin ions with ions contained in the carrier material when the ion exchange sites are uniformly distributed throughout the carrier or controlled impregnation of the carrier material with a suitable soluble tin salt under conditions selected to result in penetration of all sections of the carrier material by the tin component. One preferred method of incorporating the tin component involves coprecipitating it during the preparation of the preferred carrier material, alumina. This method typically involves the addition of a suitable soluble tin compound such as stannous or stannic chloride to an alumina hydrosol, mixing these ingredients to obtain a uniform distribution of the tin moiety throughout the sol and then combining the hydrosol with a suitable gelling agent and dropping the resulting mixture into an oil bath etc., as explained in detail hereinbefore. After drying and calcining the resulting gelled carrier material there is obtained an intimate combination of alumina and tin oxide having the required dispersion and particle size. Another preferred method of incorporating the tin component into the catalytic composite involves utilization of a soluble, decomposable compound of tin to impregnate the porous carrier material. In general, the solvent used in this impregnation step is selected on the basis of the capability to dissolve the desired tin compound and to hold the tin moiety in solution until it is evenly distributed throughout the carrier material and is preferably an aqueous, rather strongly acidic solution. Thus the tin component may be added to the carrier material by commingling the latter with an aqueous solution of a suitable tin salt or suitable compound of tin such as stannous bromide, stannous chloride, stannic chloride, stannic chloride pentahydrate, stannic chloride diamine, stannic trichloride bromide, stannic chromate, stannous fluoride, stannic fluoride, stannic iodide, stannic sulfate, stannic tartrate, and the like compounds. The acid used in the impregnation solution may be any organic or inorganic acid that is capable of maintaining the pH of the impregnation solution in the range of about -1 or less to about 3 and preferably less than 1 during the impregnation step and that does not contaminate the resultant catalyst. Suitable acids are: inorganic acids such as hydrochloric acid, nitric acid, and the like; and strongly acidic organic acids such as oxalic acid, malonic acid, citric acid, and the like. A particularly preferred impregnation solution comprises stannic or stannous chloride dissolved in a hydrochloric acid solution containing HCl in an amount corresponding to at least about 5 wt. % of the carrier material which is to be impregnated. Another useful impregnation solution is stannous or stannic chloride dissolved in an anhydrous alcohol such as ethanol. In general, the tin component can be incorporated either prior to, simultaneously with, or after the other metallic components are added to the carrier material. However, I have found that excellent results are obtained when the tin component is incorporated simultaneously with the platinum or palladium, rhenium, and rhodium components. In fact, I have determined that one preferred aqueous impregnation solution contains chloroplatinic acid, perrhenic acid, rhodium trichloride hydrate, a relatively high amount of hydrogen chloride, and stannic or stannous chloride.

Regardless of which tin compound is used in the preferred impregnation step, it is essential that the tin component be uniformly distributed throughout the carrier material. In order to achieve this objective with an aqueous impregnation solution it is necessary to dilute the impregnation solution to a volume which is approximately equal to or substantially in excess of the void volume of the carrier material which is impregnated and to add a relatively strong acid such as hydrochloric acid, nitric acid, and the like to the impregnation solution in an amount calculated to maintain the pH of the impregnation solution in a range of about -1 or less to about 3, preferably less than 1. It is preferred to use a volume ratio of impregnation solution to carrier material of at least 0.5:1 and preferably about 1:1 to about 10:1 or more. Similarly, it is preferred to use a relatively long contact time during the impregnation step ranging from about 1/4 hour up to about 1/2 hour or more before drying to remove excess solvent in order to insure a high dispersion of the tin component into the carrier material. The carrier material is, likewise, preferably constantly agitated during this preferred impregnation step.

Regarding the amount of the tin component contained in the instant composite, it is preferably sufficient to constitute about 0.01 to about 5 wt. % of the final composite, calculated on an elemental basis, although substantially higher amounts of tin may be utilized in some cases. Best results are typically obtained with about 0.1 to about 1 wt. % tin.

A third essential ingredient of the subject catalyst is the platinum or palladium component. That is, it is intended to cover the use of platinum or palladium or mixtures thereof as a third component of the present composite. It is an essential feature of the present invention that substantially all of this platinum or palladium component exists within the final catalytic composite in the elemental metallic state. Generally, the amount of this component present in the final catalytic composite is small compared to the quantities of the other components combined therewith. In fact, the platinum or palladium component generally will comprise about 0.01 to about 2 wt. % of the final catalytic composite, calculated on an elemental basis. Excellent results are obtained when the catalyst contains about 0.05 to about 1 wt. % of platinum or palladium metal.

This platinum or palladium component may be incorporated in the catalytic composite in any suitable manner known to result in a relatively uniform distribution of this component in the carrier material such as coprecipitation or cogellation, ion exchange, or impregnation. The preferred method of preparing the catalyst involves the utilization of a soluble, decomposable compound of platinum or palladium to impregnate the carrier material in a relatively uniform manner. For example, this component may be added to the support by commingling the latter with an aqueous solution of chloroplatinic or chloropalladic acid. Other water-soluble compounds of platinum or palladium may be employed in impregnation solutions and include ammonium chloroplatinate, bromoplatinic acid, platinum trichloride, platinum tetrachloride hydrate, platinum dichlorocarbonyl dichloride, dinitrodiaminoplatinum, sodium tetranitroplatinate (II), palladium chloride, palladium nitrate, palladium sulfate, diammine palladium (II) hydroxide, tetrammine palladium (II) chloride, etc. The utilization of a platinum or palladium chloride compound, such as chloroplatinic or chloropalladic acid, is preferred since it facilitates the incorporation of both the platinum or palladium component and at least a minor quantity of the halogen component in a single step. Hydrogen chloride or the like acid is also generally added to the impregnation solution in order to further facilitate the incorporation of the halogen component and the uniform distribution of the metallic components throughout the carrier material. In addition, it is generally preferred to impregnate the carrier material after it has been calcined in order to minimize the risk of washing away the valuable platinum or palladium compounds; however, in some cases it may be advantageous to impregnate the carrier material when it is in a gelled state.

Yet another essential ingredient of the present catalytic composite is a rhodium component. It is of fundamental importance that substantially all of the rhodium component exists within the catalytic composite of the present invention in the elemental metallic state or in a state which is reducible to the metallic state under hydrocarbon conversion conditions or in a mixture of these states. The rhodium component may be utilized in the composite in any amount which is catalytically effective, with the preferred amount being about 0.01 to about 2 wt. % thereof, calculated on an elemental basis. Typically, best results are obtained with about 0.01 to about 1 wt. % rhodium. It is additionally preferred to select the specified amount of rhodium from within this broad weight range as a function of the amount of the platinum or palladium component, on an atomic basis, as is explained hereinafter.

This rhodium component may be incorporated into the catalytic composite in any suitable manner known to those skilled in the catalyst formulation art which results in a relatively uniform distribution of rhodium in the carrier material. In addition, it may be added at any stage of the preparation of the composite--either during preparation of the carrier material or thereafter--and the precise method of incorporation used is not deemed to be critical. However, best results are obtained when the rhodium component is relatively uniformly distributed throughout the carrier material, and the preferred procedures are the ones known to result in a composite having this relatively uniform distribution. One acceptable procedure for incorporating this component into the composite involves cogelling or coprecipitating the rhodium component during the preparation of the preferred carrier material, alumina. This procedure usually comprehends the addition of a soluble, decoposable compound of rhodium such as rhorium trichloride hydrate or rhodium nitrate to the alumina hydrosol before it is gelled. The resulting mixture is then finished by conventional gelling, aging, drying, and calcination steps as explained hereinbefore. A preferred way of incorporating this component is an impregnation step wherein the porous carrier material is impregnated with a suitable rhodium-containing solution either before, during, or after the carrier is calcined. Preferred impregnation solutions are aqueous solutions of water soluble, decomposable rhodium compounds or complexes such as hexamminerhodium (III) chloride, rhodium carbonylchloride, rhodium trichloride hydrate, rhodium nitrate, sodium hexachlororodate (III), sodium hexanitrorhodate (III), rhodium sulfate, and the like complexes of compounds. Best results are ordinarily obtained when the impregnation solution is an aqueous solution of rhodium trichloride hydrate or rhodium nitrate. This component can be added to the carrier material either prior to, simultaneously with, or after the other metallic components are combined therewith. Best results are usually achieved when this component is added simultaneously with the platinum or palladium and rhenium coponents. In fact, excellent results are obtaned, as reported in the examples with a one step impregnation procedure using a tin-containing carrier material and an aqueous solution comprising chloroplatinic or chlorapalladic acid, rhodium trichloride hydrate, hydrochloric acid, and perrhenic acid.

It is essential to incorporate a halogen coponent into the multimetallic catalytic composite of the present invention. Although the precise form of the chemistry of the association of the halogen component with the carrier material is not entirely known, it is customary in the art to refer to the halogen component as being combined with the carrier material, or with the other ingredients of the catalyst in the form of the halide (e.g. as the chloride). This combined halogen may be either fluorine, chlorine, iodine, bromine, or mixtures thereof. Of these, fluorine and, particularly, chloride are preferred for the purposes of the present invention. The halogen may be added to the carrier material in any suitable manner, either during preparation of the support or before or after the addition of the other components. For example, the halogen may be added, at any stage of the preparation of the carrier material or to the calcined carrier material, as an aqueous solution of a suitable, decomposable halogen-containing compound such as hydrogen fluoride, hydrogen chloride, hydrogen bromide, ammonium chloride, etc. The halogen component or a portion thereof, may be combined with the carrier material during the impregnation of the latter with the platinum or palladium, rhenium, tin, or rhodium component; for example, through the utilization of a mixture of chloroplatinic acid and hydrogen chloride. In another situation, the alimina hydrosol which is typically utilized to form the preferred alumina carrier material may contain halogen and thus contribute at least a portion of the halogen component to the final composite. For reforming, the halogen will be typically combined with the carrier material in an amount sufficient to result in a final composite that contains about 0.1 to about 3.5%, and preferably about 0.6 to about 1.5%, by weight, of halogen calculated on an elemental basis. In isomerization or hydrocracking embodiments, it is generally preferred to utilize relatively larger amounts of halogen in the catalyst--typically ranging up to about 10 wt. % halogen calculated on an elemental basis, and more preferably, about 1 to about 5 wt. %. It is to be understood that the specified level of halogen component in the instant catalyst can be achieved or maintained during use in the conversion of hydrocarbons by continuously or periodically adding to the reaction zone a decomposable halogen-containing compound such as an organic chloride (e.g. ethylene dichloride, carbon tetrachloride, t-butyl chloride) in an amount of about 1 to 100 wt. ppm. of the hydrocarbon feed, and preferably about 1 to 10 wt. ppm.

Regarding the referred amounts of the various metallic components of the subject catalyst, I have found it to be a good practice to specify the amounts of the rhodium component, the tin component, and the rhenium component as a function of the amount of the platinum or palladium component. On this basis, the amount of the rhodium component is ordinarily selected so that the atomic ratio of rhodium to platinum or palladium metal contained in the composite is about 0.1:1 to about 2:1, with the preferred range being about 0.25:1 to about 1.5:1. Similarly, the amount of the rhenium component is ordinarily selected to produce a composite containing an atomic ratio of rhenium to platinum or palladium metal of about 0.05:1 to about 10:1, with the preferred range being about 0.2:1 to about 5:1. On the same basis, the amount of the tin component is preferably set at an atomic ratio of about 0.1:1 to about 3:1, with the most preferred range being about 0.25:1 to about 1.5:1.

Another significant parameter for the instant catalyst is the "total metals content" which is defined to be the sum of the platinum or palladium component, the rhodium component, the tin component, and the rhenium component, calculated on an elemental basis. Good results are ordinarily obtained with the subject catalyst when this parameter is fixed at a value of about 0.15 to about 4 wt. % with best results ordinarily achieved at a metals loading of about 0.3 to about 3 wt. %.

In embodiments of the present invention wherein the instant multimetallic catalytic composite is used for the dehydrogenation of dehydrogenatable hydrocarbons or for the hydrogenation of hydrogenatable hydrocarbons, it is ordinarily a preferred practice to include an alkali or alkaline earth metal component in the composite and to minimize or eliminate the halogen component therefrom. More precisely, this optional ingredient is selected from the group consisting of the compounds of the alkali metals--cesium, rubidium, potassium, sodium, and lithium--and the compounds of the alkaline earth metals--calcium, strontium, barium, and magnesium. Generally, good results are obtained in these embodiments when this component constitutes about 0.1 to about 5 wt. % of the composite, calculated on an elemental basis. This optional alkali or alkaline earth metal component can be incorporated in the composite in any of the known ways, with impregnation with an aqueous solution of a suitable water-soluble, decomposable compound being preferred.

An optional ingredient for the multimetallic catalyst of the present invention is a Friedel-Crafts metal halide component. This ingredient is particularly useful in hydrocarbon conversion embodiments of the present invention wherein it is preferred that the catalyst utilized has a strong acid or cracking function associated therewith--for example, an embodiment wherein hydrocarbons are to be hydrocracked or isomerized with the catalyst of the present invention. Suitable metal halides of the Friedel-Crafts type include aluminum chloride, aluminum bromide, ferric chloride, ferric bromide, zinc chloride, and the like compounds, with the aluminum halides, and particularly, aluminum chloride ordinarily yielding best results. Generally, this optional ingredient can be incorporated into the composite of the present invention by any of the conventional methods for adding metallic halides of this type; however, best results are ordinarily obtained when the metallic halide is sublimed onto the surface of the carrier material according to the preferred method disclosed in U.S. Pat. No. 2,999,074. The component can generally be utilized in any amount which is catalytically effective, with a value selected from the range of about 1 to about 100 wt. % of the carrier material generally being preferred.

Regardless of the details of how the components of the catalyst are combined with the porous carrier material, the final catalyst generally will be dried at a temperature of about 200° to about 600° F. for a period of at least about 2 to about 24 hours or more, and finally calcined or oxidized at a temperature of about 700° F. to about 1100° F. in an air or oxygen atmosphere for a period of about 0.5 to about 10 hours in order to convert substantially all of the metallic components to the corresponding oxide forms. Because a halogen component is utilized in the catalyst, best results are geneally obtained when the halogen content of the catalyst is adjusted during this oxidation step by including a halogen or a decomposable halogen-containing compound such as HCl in the air or oxygen atmosphere utilized. In particular, when the halogen component of the catalyst is chlorine, it is preferred to use a mole ratio of H₂ O to HCl of about 5:1 to about 100:1 during at least a portion of this oxidation step in order to adjust the final chlorine content of the catalyst to a range of about 0.1 to about 3.5 wt. %.

It is an essential feature of the present invention that the resultant oxidized catalytic composite is subjected to a substantially water-free and hydrocarbon-free reduction step prior to its use in the conversion of hydrocarbons. This step is designed to selectively reduce the platinum or palladium component, the rhodium component, and the rhenium component to the corresponding metals, while maintaining the tin component in a particle oxidation state, and to insure a uniform and finely divided dispersion of these metallic components throughout the carrier material. Preferably substantially pure and dry hydrogen (i.e less than 20 vol. ppm. H₂ O) is used as the reducing agent in this step. The reducing agent is contacted with the oxidized catalyst at conditions including a temperature of about 800° F. to about 1200° F. and a period of time of about 0.5 to 10 or more hours effective to reduce substantially all of the platinum or palladium to the elemental metallic state and at least a portion of the rhodium and rhenium components to the corresponding elemental metallic states, while maintaining the tin component in a positive oxidation state. This reduction treatment may be performed in situ as part of a start-up sequence if precautions are taken to predry the plant to a substantially water-free state and if substantially water-free and hydrocarbon-free hydrogen is used.

The resulting selectively reduced catalytic composite may, in some cases, be beneficially subjected to a presulfiding operation designed to incorporate in the catalytic composite from about 0.01 to about 1 wt. % sulfur, and preferably about 0.05 to about 0.5 wt. %, calculated on an elemental basis. This presulfiding treatment typically takes place in the presence of hydrogen and a suitable sulfur-containing sulfiding reagent such as hydrogen sulfide, lower molecular weight mercaptans, organic sulfides, etc. Preferably, this procedure comprises treating the selectively reduced catalyst, prior to any contact of hydrocarbon with same, with a sulfiding gas such as a mixture of hydrogen and hydrogen sulfide having about 10 moles of hydrogen per mole of hydorgen sulfide at conditions sufficient to effect the desired incorporation of sulfur, generally including a temperature ranging from about 50° F. up to about 1100° F. or more. It is generally a good practice to perform this presulfiding step under substantially water-free conditions. It is within the scope of the present invention to maintain or achieve the sulfided state of the instant catalyst during use in the conversion of hydrocarbons by continuously or periodically adding a decomposable sulfur-containing compound, such as the ones previously mentioned, to the reactor containing the catalyst in an amount sufficient to provide about 1 to about 500 wt. ppm., preferably 1 to 20 wt. ppm. of sulfur based on hydrocarbon charge.

According to the present invention, a hydrocarbon charge stock and hydrogen are contacted with a multimetallic catalyst of the type described above in a hydrocarbon conversion zone. This contacting may be accomplised by using the catalyst in a fixed bed system, a moving bed system, a fluidized bed system, or in a batch type operation; however, in view of the danger of attrition losses of the valuable catalyst and of well known operational advantages, it is preferred to use a fixed bed system or a dense-phase moving bed system such as is shown in U.S. Pat. No. 3,725,429. It is also contemplated that the contacting step can be performed in the presence of a physical mixture of particles of the catalyst of the present invention and particles of a conventional dual-function catalyst of the prior art. In the fixed bed system, a hydrogen-rich gas and the charge stock are preheated by any suitable heating means to the desired reaction temperature and then are passed into a conversion zone containing a fixed bed of the catalyst type previously characterized. It is, of course, understood that the conversion zone may be one or more separate reactors with suitable means therebetween to insure that the desired conversion temperature is maintained at the entrance to each reactor. It is also important to note that the reactants may be contacted with the catalyst bed in either upward, downward, or radial flow fashion with the latter being preferred. In addition, the reactants may be in the liquid phase, a mixed liquid-vapor phase, or a vapor phase when they contact the catalyst, with best results obtained in the vapor phase.

In the case where the multimetallic catalyst of the present invention is used in a reforming operation, the reforming system will comprise a reforming zone containing one or more fixed beds or dense-phase moving beds of the catalyst type previously characterized. In a multiple bed system it is of course within the scope of the present invention to use the present catalyst in less than all of the beds, with a conventional dual-function catalyst being use in the remainder of the beds. This reforming zone may be one or more separate reactors with suitable heating means therebetween to compensate for the endothermic nature of the reactions that take place in each catalyst bed. The hydrocarbon feed stream that is charged to this reforming system will comprise hydrocarbon fractions containing naphthenes and paraffins that boil within the gasoline range. The preferred charge stocks are those consisting essentially of naphthenes and paraffins, although in some cases aromatics and/or olefins may also be present. This preferred class includes straight run gasolines, natural gasolines, synthetic gasolines, partially reformed gasolines, and the like. On the other hand, it is frequently advantageous to charge thermally or catalytically cracked gasolines or higher boiling fractions thereof. Mixtures of straight run and cracked gasolines can also be used to advantage. The gasolne charge stock may be a full boiling gasoline having an initial boiling point of from about 50° F. to about 150° F. and an end boiling point within the range of from about 325° F. to about 425° F., or may be a selected fraction thereof which generally will be a higher boiling fraction commonly referred to as a heavy naphtha--for example, a naphtha boiling in the range of C₇ to 400° F. In some cases it is also advantageous to charge pure hydrocarbons or mixtures of hydrocarbons that have been extracted from hydrocarbon distillates--for example, straight-chain paraffin--which are to be converted to aromatics. It is preferred that these charge stocks be treated by conventional catalytic pretreatment methods such as hydrorefining, hydrotreating, hydrodesulfurization, etc., to remove substantially all sulfurous, nitrogenous, and water-yielding contaminants therefrom and to saturate any olefins that may be contained therein.

In other hydrocarbon conversion embodiments, the charge stock will be of the conventional type customarily used for the particular kind of hydrocarbon conversion being effected. For example, in a typical isomerization embodiment the charge stock can be a paraffinic stock rich in C₄ or C₈ normal paraffins, or a normal butane-rich stock, or a n-hexane-rich stock, or a mixture of xylene isomers, etc. In a dehydrogenation embodiment, the charge stock can be any of the known dehydrogenatable hydrocarbons such as an aliphatic compound containing 2 to 30 carbon atoms per molecule, a C₄ to C₃₀ normal paraffin, a C₈ to C₁₂ alkylaromatic, a naphthene, and the like. In hydrocracking embodiments, the charge stock will be typically a gas oil, heavy cracked cycle oil, etc. In addition alkylaromatic, olefins, and naphthenes can be conveniently isomerized by using the catalyst of the present invention. Likewise, pure hydrocarbons or substantially pure hydrocarbons can be converted to more valuable products by using the acidic multimetallic catalyst of the present invention in any of the hydrocarbon conversion processes, known to the art, that use a dual-function catalyst.

In a reforming embodiment, it is generally preferred to utilize the novel multimetallic catalytic composite in a substantially water-free environment. Essential to the achievement of this condition in the reforming zone is careful control of the water level present in the charge stock and in the hydrogen stream which are charged to the zone. Best results are ordinarily obtained when the total amount of water entering the conversion zone from any source is held to a level less than 50 ppm., and preferably less than 20 ppm., expressed as weight of equivalent water in the charge stock. In general, this can be accomplished by careful control of the water present in the charge stock and in the hydrogen stream. The charge stock can be dried by using any suitable drying means known to the art, such as a conventional solid adsorbent having a high selectivity for water, for instance, sodium or calcium crystalline aluminosilicates, silica gel, activated alumina, molecular sieves, anhydrous calcium sulfate, high surface area sodium, and the like adsorbents. Similarly, the water content of the charge stock may be adjusted by suitable stripping operations in a fractionation column or like device. And in some cases, a combination of adsorbent drying and distillation drying may be advantageously to effect almost complete removal of water from the charge stock. Preferably, the charge stock is dried to a level corresponding to less than 20 ppm. of H₂ O equivalent. In general, it is preferred to maintain the hydrogen stream entering the hydrocarbon conversion zone at a level of about 10 vol. ppm. of water of less. If the water level in the hydrogen stream is too high, drying of same can be conveniently accomplished by contacting the hydrogen stream with a suitable desiccant such as those mentioned above.

In the reforming embodiment, an effluent stream is withdrawn from the reforming zone and passed through a cooling means to a separation zone, typically maintained at about 25° to 150° F., wherein a hydrogen-rich gas is separated from a high octane liquid product, commonly called an unstabilized reformate. When a super-dry operation is desired, at least a portion of this hydrogen-rich gas is withdrawn from the separatng zone and passed through an adsorption zone containing an adsorbent selective for water. The resultant substantially water-free hydrogen stream can then be recycled through suitable compressing means back to the reforming zone. The liquid phase from the separating zone is typically withdrawn and commonly treated in a fractionating system in order to adjust the butane concentration, thereby controlling front-end volatility of the resulting reformate.

The conditions utilized in the numerous hydrocarbon conversion embodiments of the present invention are those customarily used in the art for the particular reaction, or combination of reactions, taht is to be effected. For instance, alkylaromatic, olefin, and paraffin isomerization conditions include: a temperature of about 32° F. to about 1000° F., and preferably from about 75° to about 600° F.; a pressure of atmospheric to about 100 atmospheres, a hydrogen to hydrocarbon mole ratio of about 0.5:1 to about 20:1, and an LHSV (calculated on the basis of equivalent liquid volume of the charge stock contacted with the catalyst per hour divided by the volume of conversion zone containing catalyst) of about 0.2 hr.⁻ ¹ to 10 hr.⁻ ¹ . Dehydrogenation conditions include: a temperature of about 700° to about 1250° F., a pressure of about 0.1 to about 10 atmospheres, a liquid hourly space velocity of about 1 to 40 hr.⁻ ¹, and a hydrogen to hydrocarbon mole ratio of about 1:1 to 20:1. Likewise, typically hydrocracking conditions include: a pressure of about 500 psig. to about 3000 psig., a temperature of about 400° F. to about 900° F., an LHSV of about 0.1 hr.⁻ ¹ to about 10 hr.⁻ ¹, and hydrogen circulation rates of about 1000 to 10,000 SCF per barrel of charge.

In the reforming embodiment of the present invention, the pressure utilized is selected from the range of about 0 psig. to about 1000 psig., with the preferred pressure being about 50 psig. to about 600 psig. Particularly good results are obtained at low pressure; namely, a pressure of about 50 to 350 psig. In fact, it is a singular advantage of the present invention that it allows stable operation at lower pressure than have heretofore been succesfully utilized in so-called "continuous" reforming systems (i.e. reforming for periods of about 15 to about 200 or more barrels of charge per pound of catalyst without regenertion) with all platinum monometallic catalyst. In other words, the multimetallic catalyst of the present invention allows the operation of a continuous reforming system to be conducted at lower pressure (i.e. 100 to about 350 psig.) for about the same or better catalyst life before regeneration as has been heretofore realized with conventional monometallic catalysts at higher pressures (i.e. 400 to 600 psig.). On the other hand, the stability feature of the present invention enables reforming operations conducted at pressures of 400 to 600 psig. to achieve substantially increased catalyst life before regeneration.

Similarly, the temperature required for reforming is generally lower than that required for a similar reforming operation using a high quality catalyst of the prior art. This significant and desirable feature of the present invention is a consequence of the selectivity of the multimetallic catalyst of the present invention for the octane-upgrading reactions that are preferably induced in a typical reforming operation. Hence, the present invention requires a temperture in the range of from about 800° F. to about 1100° F. and preferably about 900° F. to about 1050° F. As is well known to those skilled in the continuous reforming art, the initial selection of the temperature within this broad range is made primarily as a function of the desired octane of the product reformate considering the characteristics of the charge stock and of the catalyst. Ordinarily, the temperature then is thereafter slowly increased during the run to compensate for the inevitable deactivation that occurs to provide a constant octane product. Therefore, it is a feature of the present invention that the rate at which the temperature is increased in order to maintain a constant octane product is substantially lower for the catalyst of the present invention than for a high quality reforming catalyst which is manufactured in exactly the same manner as the catalyst of the present invention except for the inclusion of the rhodium, tin, and rhenium components. Moreover, for the catalyst of the present invention, the C₅ + yield loss for a given temperature increase is substantially lower than for a high quality reforming catalyst of the prior art. The reforming embodiment of the present invention also typically utilizes sufficient hydrogen to provide an amount of about 1 to about 20 moles of hydrogen per mole of hydrocarbon entering the reforming zone, with excellent results being obtained when about 5 to about 10 moles of hydrogen are used per mole of hydrocarbon. Likewise, the liquid hourly space velocity (LHSV) used in reforming is selected from the range of about 0.1 to about 10 hr.⁻ ¹, with a value in the range of about 1 to about 5 hr.⁻ ¹ being preferred. In fact, it is a feature of the present invention that it allows operations to be conducted at higher LHSV than normally can be stably achieved in a continuous reforming process with a high quality reforming catalyst of the prior art. This last feature is of immense economic significance because it allows a continuous reforming process to operate at the same throughput level with less catalyst inventory than that heretofore used with conventional reforming catalysts at no sacrifice in catalyst life before regeneration.

The following working examples are given to illustrate further the preparation of the acidic multimetallic catalytic composite of the present invention and the use thereof in the conversion of hydrocarbons. It is understood that the examples are intended to be illustrative rather than restrictive.

EXAMPLE I

A tin-containing alumina carrier material comprising 1/16 inch spheres is prepared by: forming an aluminum hydroxyl chloride sol by dissolving substantially pure aluminum pellets in a hydrochloric acid solution, adding stannic chloride to the resulting sol in an amount selected to result in a finished catalyst containing about 0.5 wt. % tin, adding hexamethylenetetramine to the resulting sol, gelling the resulting solution by dropping it into an oil bath to form spherical particles of an aluminum hydrogen, containing tin in a particle size which is less than 100 Angstroms in maximum dimension, aging and washing the resulting particles, and finally drying and calcining the aged and washed spherical particles of gamma-alumina containing about 0.3 weight percent combined chloride and a uniform dispersion of about 0.5 wt. % tin in the form of tin oxide. Additional details as to this method of preparing the preferred carrier material are given in the teachings of U.S. Pat. No. 2,620,314.

An aqueous acidic impregnation solution containing chloroplatinic acid, perrhenic acid, rhodium trichloride hydrate, and hydrogen chloride is the prepared. The tin-containing alumina carrier material is thereafter admixed with the impregnation solution. The amount of reagent contained in this impregnation solution is calculated to result in a final composite containing, on an elemental basis, 0.3 wt. % platinum, 0.3 wt. % rhenium, and 0.1 wt. % rhodium. In order to insure uniform dispersion of the metallic components throughout the carrier material, the amount of hydrochloric acid used is about 3 wt. % of the alumina particles. This impregnation step is performed by adding the carrier material particles to the impregnation mixture with constant agitation. In addition, the volume of the solution is approximately the same as the void volume of the carrier material particles. The impregnation mixture is maintained in contact with the carrier material particles for a period of about 1/2 to about 3 hours at a temperature of about 70° F. Thereafter, the temperature of the impregnation mixture is raised to about 225° F. and the excess solution was evaporated in a period of about 1 hour. The resulting dried impregnated particles are then subjected to an oxidation treatment in a sulfur-free dry air stream at a temperature of about 975° F. and GHSV of about 500 hr.⁻ ¹ for about 1/2 hour. This oxidation step is designed to convert substantially all of the metallic ingredients to the corresponding oxide forms. The resulting oxidized spheres are subsequently contacted in a halogen treating step with a sulfur-free air stream containing H₂ O and HCl in a mole ratio of about 30:1 for about 2 hours at 975° F. and a GHSV of about 500 hr.⁻ ¹ in order to adjust the halogen content of the catalyst particles to a value of about 1 wt. %. The halogen-treated spheres are thereafter subjected to a second oxidation step with a dry sulfur-free stream at 975° F. and a GHSV of 500 hr.⁻ ¹ for an additional period of about 1/2 hour.

The oxidized and halogen-treated catalyst particles are then subjected to a dry prereduction treatment, designed to reduce substantially all of the platinum component to the corresponding elemental metallic state and at least a portion of the rhenium and rhodium components to the elemental metallic state, while maintaining substantially all of the tin component in a positive oxidation state, by contacting them for about 1 hour with a substantially hydrocarbon-free and sulfur-free hydrogen stream containing less than 5 vol. ppm. H₂ O at a temperature of about 1050° F., a pressure slightly above atmospheric, and a flow rate of the hydrogen stream through the catalyst particles corresponding to a gas hourly space velocity of about 400 hr.⁻ ¹.

A sample of the resulting reduced catalyst particles is analyzed and found to contain, on an elemental basis, about 0.3 wt. % platinum, about 0.3 wt. % rhenium, about 0.1 wt. % rhodium, about 0.5 wt. % tin, and about 1 wt. % chloride. This corresponds to an atomic ratio of rhenium to platinum of 1.05:1, of rhodium to platinum of 0.63:1, and of tin to platinum of 2.74:1.

EXAMPLE II

A portion of the spherical acidic multimetallic catalyst particles produced by the method described in Example I is loaded into a scale model of a continuous, fixed bed reforming plant of conventional design. In this plant a heavy Kuwait naphtha and hydrogen are continuously contacted at reforming conditions: a liquid hourly space velocity of 3.0 hr.⁻ ¹, a pressure of 250 psig., a hydrogen to hydrocarbon mole ratio of 8:1, and a temperature sufficient to continuously produce a C₅ + reformate having an octane number of 100 F-1 clear. It is to be noted that these are exceptionally severe conditions.

The heavy Kuwait naphtha has an API gravity at 60° F. of 60.4, an initial boiling point of 184° F., a 50% boiling point of 256° F., and an end boiling point of 360° F. In addition, it contains about 8 vol. % aromatics, 71 vol. % paraffins, 21 vol. % naphthenes, 0.5 weight parts per million sulfur, and 5 to 8 weights parts per million water. The F-1 clear octane number of the raw stock is 40.0.

The fixed bed reforming plant is made up of a reactor containing the acidic multimetallic catalyst, a hydrogen separation zone, a debutanizer column, and suitable heating, pumping, cooling, and controlling means. In this plant, a hydrogen recycle stream and the charge stock are commingled and heated to the desired temperature. The resultant mixture is then passed downflow into a reactor containing the subject catalyst as a fixed bed. An effluent stream is then withdrawn from the bottom of the reactor, cooled to about 55° F., and passed to a separating zone wherein a hydrogen-rich gaseous phase separates from a liquid hydrocarbon phase. A portion of the gaseous phase is continuously passed through a high surface sodium scrubber and the resulting water-free hydrogen-containing stream recycled to the reactor in order to supply hydrogen thereto, and the excess gaseous phase over that needed for plant pressure is recovered as excess separator gas. The liquid hydrocarbon phase from the hydrogen separating zone is withdrawn therefrom and passed to a debutanizer column of conventional design wherein light ends are taken overhead as debutanizer gas and a C₅ + reformate stream recovered as bottoms.

The test run is continued for a catalyst life of about 10 barrels of charge per pound of catalyst utilized, and it is determined that the activity, selectivity, and stability characteristics of the present acidic multimetallic catalyst are vastly superior to those observed in a similar type test with a conventional commercial reforming catalyst. More specifically, the results obtained from the subject catalyst are superior to the platinum metal-containing catalyst of the prior art in the area of initial temperature required to make target octane, average C₅ + yield at octane, average rate of temperature increase necessary to maintain octane, and C₅ + yield decline rate.

It is intended to cover by the following claims, all changes and modifications of the above disclosure of the present invention which would be self-evident to a man of ordinary skill in the catalyst formulation art or the hydrocarbon conversion art. 

I claim as my invention:
 1. A process for converting a hydrocarbon which comprises contacting the hydrocarbon at hydrocarbon conversion conditions with an acidic catalytic composite comprising a porous carrier material containing, on an elemental basis, about 0.01 to about 2 wt. % platinum or palladium, about 0.01 to about 2 wt. % rhodium, about 0.01 to about 2 wt. % rhenium, about 1.01 to about 5 wt. % tin, and about 0.1 to about 3.5 wt. % halogen, wherein the platinum or palladium, rhodium, rhenium, and tin are uniformly dispersed throughout the porous carrier material, wherein substantially all of the platinum or palladium rhodium and rhenium are present in the corresponding elemental metallic states and wherein substantially all of the tin is present in an oxidation state above that of the elemental metal and in a particle size which is less than 100 Angstroms in maximum dimension.
 2. A process as defined in claim 1 wherein the porous carrier is a refractory inorganic oxide.
 3. A process as defined in claim 2 wherein the refractory inorganic oxide is alumina.
 4. A process as defined in claim 1 wherein the halogen is combined chloride.
 5. A process as defined in claim 1 wherein the atomic ratio of rhodium to platinum or palladium contained in the composite is about 0.1:1 to about 2:1.
 6. A process as defined in claim 1 wherein the atomic ratio of rhenium to platinum or palladium contained in the composite is about 0.05:1 to about 10:1.
 7. A process as defined in claim 1 wherein the atomic ratio of tin to platinum or palladium contained in the composite is about 0.1:1 to about 3:1.
 8. A process as defined in claim 1 wherein substantially all of the tin is present in the catalytic composite as tin oxide.
 9. A process as defined in claim 1 wherein the composite contains about 0.05 to about 1 wt. % platinum, about 0.05 to about 1 wt. % rhodium, about 0.05 to about 1 wt. % rhenium, about 0.05 to about 1 wt. % tin, and about 0.5 to about 1.5 wt. % halogen.
 10. A process as defined in claim 1 wherein the contacting of the hydrocarbon with the catalytic composite is performed in the presence of hydrogen.
 11. A process as defined in claim 1 wherein the type of hydrocarbon conversion is catalytic reforming of a gasoline fraction to produce a high octane reformate, wherein the hydrocarbon is contained in the gasoline fraction, wherein the contacting is performed in the presence of hydrogen and wherein the hydrocarbon conversion conditions are reforming conditions.
 12. A process as defined in claim 11 wherein the reforming conditions include a temperature of about 800° to about 1100° F., a pressure of about 0 to about 1000 psig., a liquid hourly space velocity of about 0.1 to about 10 hr.⁻ ¹, and a mole ratio of hydrogen to hydrocarbon of about 1:1 to about 20:1.
 13. A process as defined in claim 11 wherein the contacting is performed in a substantially water-free environment.
 14. A process as defined in claim 11 wherein the reforming conditions include a pressure of about 50 to about 350 psig.
 15. A process as defined in claim 9 wherein the type of hydrocarbon conversion is catalytic reforming of a gasoline fraction to produce a high octane reformate, wherein the hydrocarbon is contained in the gasoline fraction, wherein the contacting is performed in the presence of hydrogen, and wherein the hydrocaron conversion conditions are reforming conditions.
 16. An acidic catalytic composite comprising a porous carrier material containing, on an elemental basis, about 0.01 to about 2 wt. % platinum or palladium, about 0.01 to about 2 wt. % rhodium, about 0.01 to about 2 wt. % rhenium, about 0.01 to about 5 wt. % tin, and about 0.1 to about 3.5 wt. % halogen, wherein the platinum or palladium, rhodium, rhenium, and tin are uniformly dispersed throughout the porous carrier material, wherein substantially all of the platinum or palladium rhodium and rhenium are present in the corresponding elemental metallic states, and wherein substantially all of the tin is present in an oxidation state above that of the elemental metal and in a particle size which is less than 100 Angstroms in maximum dimension. 